型式/ Type : 弱酸型阳离子交换树脂/Weak acid cation exchange resin 结构/ Matrix structure : 巨孔状交叉键结聚苯乙烯/ Macroporous crosslinked polystyrene 官能基/ Functional group : Iminodiacetic 物理型式/ Physical form : 含水球状/ Moist spherical beads 离子型式/ Ionic as shipped : 钠/ Sodium 粒径分布/ Screen size USS(wet) : 16 to 50 粒径大小/ Particle size : 0.3 to 1.2 mm 总交换⊙容量/Total Exc. Capacity : 1.8 meq/ml (H+) 膨胀系数/ Swelling (approx.) : H+ → Na+ 20% 含水份/ Moisture : 45-50% pH 作范围/ Suitable pH range : 0 to 14 溶解率/Solubility : 不溶解于任何溶剂/ Insoluble in common solvents 逆洗沉降密度/Backwash settled density : 0.72 to 0.79 g/ml
建议』操作条件/ OPERATING CONDITIONS
最大操作温度/ Max .Operating Temperature : 70oC 流速/ Service flow : 10 – 30 BV/hr 逆洗膨胀空间/Backwash expansio ace : 50 to 70% 逆洗流速/ Backwash expansion flow : 8-10 BV/hr 再生/ Regeneration 酸浓度/ Concentration of acid : 5 - 8% 流速/ Flow rate : 3 – 4 BV/hr 再生酸药剂╳量/ Regeneration quantity: 150-200 g/lit of HCl :200-250g/lit of H2SO4 慢洗流速/ Rinse flow rate : 3 – 4 BV/hr 若需要转成Na离子/ Conversion to sodium form if required 浓度/ Concentration : 2-4% 流速/ Flow : 4 BV/hr 盐药量/ NaOH quantity : 50-150 g/lit 慢洗流速/ Rinse flow rate : 3 – 4 BV/hr
应用附注/ APPLICATION NOTE
金属离子的选择性是依据进流液的pH 而决定在某♀些的pH 范围内, 交换容量会很严重的下降.
最有效的除铜pH : 3 - 4 Effective pH for copper removal 最有效的除镍pH : 3 - 5 Effective pH for nickel removal 最有效的『除铁pH : 2 - 4 Effective pH for iron removal 最有效的除铅pH : 2 以上 Effective pH for lead removal 最有效的除锰pH : 4 以上 Effective pH for manganese 选择性的顺序如下: Order of selectivity is as follows Cu > Pb > Ni > Zn > Co > Cd > Fe+3 > Mn > Mg > Ca >> Na 再生药剂的选择可用盐酸或硫。对于除〓铜应用, 建议用硫酸! 建议用硷NaOH 再生将树脂转换成Na 型, 并将pH 变成原来的进水条件。 若仍有技术上的资料需求, 请与我们联络: